Pure zinc is to be diffused into copper by dipping copper into molten zinc at 450°C. Calculate how long it would take to obtain 10 wt% zinc at a depth of 0.5 mm beneath the copper surface. Is this commercially feasible? What practical problems might arise if we raise the temperature to 1000°C? Use Table for error function values as needed. At 450°C, the diffusion colficient D = 6.3 x 10-13 cm2/s. Z erf (z) Z erf (z) Z erf (z) 0 0 0.55 0.5633 1.3 0.9340 0.025 0.0282 0.60 0.6039 1.4 0.9523 0.05 0.0564 0.65 0.6420 1.5 0.9661 0.10 0.1125 0.70 0.6778 1.6 0.9763 0.15 0.1680 0.75 0.7112 1.7 0.9838 0.20 0.2227 0.80 0.7421 1.8 0.9891 0.25 0.2763 0.85 0.7707 1.9 0.9928 0.30 0.3286 0.90 0.7969 2.0 0.9953 0.35 0.3794 0.95 0.8209 2.2 0.9981 0.40 0.4284 1.0 0.8427 2.4 0.9993 0.45 0.4755 1.1 0.8802 2.6 0.9998 0.50 0.5205 1.2 0.9103 2.8 0.9999